Extrusion-grade TPE
Products Characterization:
Smooth & matt surface, excellent hand-feeling. Good tensile strength and elasticity. Halogen-free, meet RoHS demand.
Application
Mobile/MP3 earphone wire. Computer signal wire. PS2 terminated line. Audio & video signal terminated wire.
TPE TPEE extrusion guidance:
1. Previous drying of the product 2 hours at 80℃
2. The speed of the extruder is 20-80 rpm
3. Typical extrusion temperature suggested
| Section 1 | Section 2 | Section 3 | Section 4 | DIE |
| 180-200℃ | 185-205℃ | 190-210 ℃ | 190-220 ℃ | 180-200 ℃ |
Adjust processing temperature according to as the extruder screw
| TPE TPEE Technical Data Sheet | Model | ||||
| Material Properties | Test Standard | Test Condition | Unit | 2575F-ESS-1004T | |
| General Characteristics | Material Category | - | - | - | |
| Appearance(Light/Semi-matte/Frosted) | - | - | - | ||
| Extrusion/Injection | - | - | - | ||
| Physical Characteristics | Hardness | ISO 48 | 15S | Shore A | 76 |
| Proportion | ISO 1183 | - | g/cm³ | 1.001 | |
| Melt Index | ISO 1133-1:2011 | 190℃/2.16kg | g/10min | 2.4 | |
| Brittle Temperature | ISO 812 | - | ℃ | ||
| Mechanical Properties | Elongation | ISO37:2017 | 200mm/min | % | 620 |
| Tensile Strength | ISO37:2017 | 200mm/min | Mpa | 13.798 | |
| Tearing Strength | ISO34-1:2015 | 500mm/min | KN/m | ||
| Hot Air Aging | Elongation Retention Rate | ISO37:2017 | - | % | |
| Tensile Strength Retention Rate | ISO37:2017 | - | % | ||
| Electrical Performance | Volume Resistivity | ASTM D257 | - | Ohm-cm | |
| Permittivity | ASTM D150 | - | - | ||
| Combustion Performance | Vertical Burning Test | UL 94 | 3.0/6.0mm | - | |
| Oxygen Index | ASTM D2863 | - | % | ||